Effective corrosion protection for metal parts

The AUTO-K Zinc Aluminium Spray offers reliable protection against corrosion for metal parts exposed to water and weather. Thanks to the combination of zinc and aluminium, this spray forms a durable layer that protects the metal from rust.

Versatile for various applications

This spray is ideal for repairing damaged zinc surfaces and coating the inner edges of sheet metal during spot welding. Applications include:

• Heating systems
• Pipes
• Steel constructions
• Radiators
• Railings
• Guardrails

Fast-drying and heat-resistant

With a quick drying time, the treated surface is dust-dry after 5 to 10 minutes and touch-dry after 30 to 40 minutes. Full curing is achieved within 24 hours. In addition, the spray is heat-resistant up to 400°C, making it suitable for applications exposed to high temperatures.

Easy application without primer

The AUTO-K Zinc Aluminium Spray requires no pretreatment with primers and no post-treatment with other topcoats or clear lacquers. This makes application simple and efficient. For optimal protection, it is recommended to apply 2 to 3 layers, with a drying time of about 10 minutes per layer.

Technical specifications

• Binder base: Acrylic resins
• Colour: Silver-grey
• Content: 400 ml
• Spray coating: With 2 cross coats: 30-40 μm

Important usage instructions

For best results:

• Thoroughly clean and de-rust the surface.
• Shake the spray can well before use.
• Apply 2 to 3 layers with a drying time of 10 minutes per layer.

Note: do not spray on surfaces coated with synthetic resins, as the paint may wrinkle.

Overpaintability and chemical resistance

The spray can be overpainted with itself after about 10 minutes. For overpainting with other Auto-K paints, it is recommended to test first on a sample piece. In addition, the spray offers good chemical resistance, contributing to the durability of the protective layer.